Tetrasulfide Silane Coupling Agent Crosile®69 for Rubber
Bis-[γ-(triethoxysilyl)-propyl]-tetrasulfide Silane for Rubber
Chemical Properties
Silane coupling agent Crosile®69 Bis[3-(triethoxysilyl)propyl]tetrasulfide (TESPTS) is commonly used as a crosslinking agent and reinforcing filler in rubber manufacturing. TESPT Crosile®69 films provide corrosion protection to metal substrates. It is also used as a precursor for the synthesis of mesoporous silicones.
Equivalent Type
Bis(3-triethoxysilylpropyl)tetrasulfane,Bis(3-(ethoxysilyl)propyl)tetrasulfide,Bis(triethoxysilylpropyl)tetrasulfane,Bis[3-(triethoxysilyl)propyl]tetrasulfide,Xiameter OFS 6940,Couplink 89,Tetrasulfane, Bis(3-Triethoxysilylpropyl)-,Silane coupling agent Si 69 (Evonik), Z-6940(Dow Corning), A-1289 (Momentive), KBE-846 (Shin- Etsu), TESPT,Silquest A 1289,Luvomaxx TESPT,Kh 845-4-2,Silane Si69,Bis-(γ-triethoxysilylpropyl)-tetrasulfide,Coupling Agent-Si-69,SCA98,HP669, JH-69
Specifications
| Properties |
Units |
Target Values (Spec,Limits) |
| Alcohol content |
%(wt) |
≤0.5% |
| CLPTES Content |
%(wt) |
≤3.0% |
| Other impurity content |
%(wt) |
≤1.0% |
| Viscosity 25°C (cps) |
Cps |
≤14.0 |
| Sulfur Content |
%(wt) |
22.5(21.7-23.3) |
| Average chain Length |
3.70(3.55-3.85) |
|
| S2 content |
% ( wt) |
18.0 (15.0-21.0) |
| محتوای S3 |
% (وزنی) |
30.0 (27.0-33.0) |
| محتوای S4 |
% (وزنی) |
24.0 (21.0-27.0) |
| محتوای S5 تا S8 |
% (وزنی) |
27.0 (24.0-30.0) |
| فرار (100 درجه سانتیگراد / 10 دقیقه) |
% | ≤ 1.0٪ |
| وزن مخصوص (25 درجه سانتیگراد) |
0.020 ± 1.080 |
|
| ضریب شکست (25 درجه سانتیگراد) |
0.020 ± 1.480 |
|
کاربرد
بیس[γ-(تری اتوکسی سیلیل) پروپیل] تترا سولفید، بیس-[γ-(تری اتوکسی سیلیل)-پروپیل]-تترا سولفید، عامل جفت کننده سیلان Si-69، عامل جفت کننده سیلان A-1289، عامل جفت کننده سیلان KH-858، Bis- -(triethoxysilylpropyl)]-tetrasulfide